1 / 2
$1750.00
≥1 Ton
$1700.00
≥50 Ton
Model No. : | JIS G3445 |
---|---|
Brand Name : | Torich |
standard : | Gb,Astm,Jis,Din,Api |
Ningbo, Zhejiang, China
Opis produktu
Automatyczny układ wydechowy STKM11A SPARTED RURE
1. Petails:
application |
Automobile and motorcycle Shock Absorber Pipe Hydraulic-cylinder Pipe Mechanical steel pipes for auto and motor parts Gas Spring pipe motor casing pipe |
size |
length--2~12m WT--2~5mm OD--10-20mm |
material | STKM11A |
Production process | ordinary high-frequency welded pipe |
Advantages | small diameter and thick wall |
Surface Quality | The internal and external surfaces of the steel tube are not allowed to have cracks, scabs, folds, delaminations, laps, and burns. Allows for scribes, scratches, misalignment of welds, burns, oxide scales, and external burr removal traces that are not more than a negative wall thickness deviation |
Inspection items |
chemical composition Tensile test Ultrasonic examination Eddy current flaw detection Bending test Flattening test |
2.P Niezbędna tolerancja średnicy zewnętrznej i grubości ściany (mm)
Type of steel Tube | Dimension of steel tube | Permissible tolerance | ||
Average class | High class | |||
Hot-rolled (extruded and expanded) tube |
Outer diameter D | All |
±1% (min.+/-0.50) |
- |
Wall thickness | All |
+15%/-12.5% (min.+4.5/-4.0) |
- | |
Cold-drawn (cold-rolled) tube | Outer diameter D | 6~10 | ±0.2 | ±0.15 |
>10~30 | ±0.40 | ±0.20 | ||
>30~50 | ±0.45 | ±0.30 | ||
>50 | ±1% | ±0.8% | ||
Wall thickness | <1 | ±0.15 | ±0.12 | |
>1~3 |
+15% -10% |
+12.5% -10% |
||
>3 |
+12.5% -10% |
±10% | ||
Note: For hot-expanded tubes with outer diameter>35mm,the permissible tolerance of wall thickness is±18%. |
3. Longitudinal mechaniczne właściwości stalowych rur
NO. | Steel Grade | Tensile Strength(Mpa) | Yield point(Mpa) | Elongation after breaking(%) | |
s<16 | s>16 | ||||
Not less than | |||||
1 | 10 | 335~475 | 205 | 195 | 24 |
2 | 20 | 410~550 | 245 | 235 | 20 |
3 | Q295 | 430~610 | 295 | 285 | 22 |
4 | Q345 | 490~665 | 325 | 315 | 21 |
4.P Odchylenia analizy produktu od określonych granic:
Element | Limiting values for cast analysis | Permissible deviatioon of the product analysis in % by mass |
C | ≤0.22 | +0.02 |
Si | ≤0.55 | +0.05 |
Mn | ≤1.60 | +0.10 |
P | ≤0.025 | +0.005 |
S | ≤0.015 | +0.003 |
Al | ≥0.025 | -0.005 |
5. Współczynnik:
Ningbo, Zhejiang, China
Wyślij swoje zapytanie do tego dostawcy